PA66 13G15旭化成

PA66 13G15旭化成---13g15 is a polyamide 66 (nylon 66) product containing 15% glass fiber reinforcement. It is available in North America, Africa and the Middle East, Europe or Asia Pacific. Leona ™  The application fields of 13g15 include automotive industry, electrical / electronic application and Engineering / industrial accessories.
Features include:
Flame retardant / rated flame
High stiffness
high strength
Creep resistance

Fatigue resistance

Unit system test method for physical properties after drying and adjustment
Specific gravity: 1.25 -- g / cm 3, ASTM D792, ISO 1183
Shrinkage internal method
Vertical flow direction 1.2 --% internal method
Flow direction 0.70 --% internal method
Water absorption
Saturated, 23 ° C -- 2.1%
Balanced, 23 ° C, 50% RH -- 2.1% ISO 62
Unit system test method for hardness, drying and adjustment
Rockwell hardness
Grade m 94.71 ASTM d785
Grade r 120 -- ASTM d785
M scale 94.71 ISO 2039-2
R scale 120 -- ISO 2039-2
Mechanical properties - unit system test method after drying and adjustment
Tensile modulus (23 ° C) 5800 3600 MPa ISO 527-2
Tensile stress
Yield, 23 ° C -- 77.0 MPa ISO 527-2
Fracture, 23 ° C 107 73.0 MPa ISO 527-2
-- 108 79.0 MPa ASTM D638
Tensile strain
Yield, 23 ° C -- 6.0% ISO 527-2
Fracture: 2.5 8.0% ASTM D638
Fracture, 23 ° C 2.5 11% ISO 527-2
Bending modulus
-- 4900 2500 MPa ASTM D790
23°C 4800 3300 MPa ISO 178
bending strength 
-- 167 108 MPa ASTM D790
23°C 162 116 MPa ISO 178
Tiber abrasion resistance (1000 cycles) - 9.00 mg ASTM d1044
Impact performance - unit system test method after drying and adjustment
Notched impact strength of simply supported beam: 6.0 5.0 kJ / M? ISO 179
Notchless impact strength of simply supported beam: 26.38 kJ / M? ISO 179
The notched impact strength of cantilever beam is 49.59 J / m, ASTM D256